Bambu PPA-CF

At 3D Printer Gear, an authorized reseller of Bambu products, we present Bambu PPA-CF—premium fiber-reinforced nylon that delivers industrial-grade printing quality with precise 1:1 reproduction. Renowned for its exceptional mechanical properties and reliable performance in humid or high-temperature environments, Bambu PPA-CF is ideal for engineering applications, from mechanical prototypes to automotive components. Additionally, its broad printer compatibility sets a new standard for professional engineering filaments. Experience the power of Bambu PPA-CF and bring your designs to life!

Cautions for Use

• 0.2 mm Nozzle Not Compatible
• Hardened Steel Nozzle Mandatory
• AMS & AMS lite NOT Compatible
• Must Be Dried before Use to Achieve Optimal Print Quality

 

 

Metal-Like Strength

PPA-CF offers strength approaching metal levels, being 48% stronger and 102% stiffer than normal PA6-CF. This filament excels in mechanical properties, making it ideal for high-performance engineering applications. Perfect for repairs, it can effectively replace automotive and industrial parts with exceptional durability and reliability.

 

Industrial-Grade Precision

Achieve industrial-grade precision with Bambu PPA-CF. Its superior dimensional stability ensures that your high-precision prototypes match your design drawings exactly, without warping or deformation. Rely on PPA-CF for the accuracy you need in every project.

 

Stable Performance in Humid Conditions

Bambu PPA-CF supports long-term, stable use in humid environments, even underwater. With a moisture absorption rate 66% lower than normal PA6-CF, it maintains its stiffness and thermal properties over time. Whether printing propellers, customizing surfboards, or any other water-resistant application, PPA-CF delivers reliable performance.

 

Unmatched Performance Under High Temperatures

Bambu PPA-CF boasts unmatched heat resistance, capable of withstanding prolonged exposure to temperatures up to 227°C without compromising its structural integrity or performance. This makes it ideal for industrial, mechanical, or automotive parts that must tolerate ultra-high temperatures.

 

 

 

Compatible with a Wide Range of Printers

Bambu PPA-CF is compatible with P1S, X1C, and X1E printers, requiring only an enclosure and a hardened steel nozzle. This filament is easier to use than you might think, printing smoothly at nozzle temperatures between 280°C and 310°C. Expand your possibilities with Bambu PPA-CF.

 

Parameters Comparison

Note: Information on Testing Samples in Both Dry and Wet Conditions. Dimension is 80 * 10 * 4 mm³, Sparse Fill Pattern is Concentric, Sparse Fill Density is 100%.

The performance of prints depends not only on the printer and printing temperature but also on the product's orientation (XY direction is significantly better than the Z direction), wall loops, sparse infill pattern, sparse infill density, size, structure, shape, and other factors.

 

Accessory Compatibility

 

Downloads

Filament TDS

Filament MSDS

Filament RoHS

 

Printing Tips

Drying Recommendations:

• Drying Temperature:

In a blast drying oven: 100°C to 140°C for 8 to 12 hours.

On an X1 printer's heatbed: 110°C to 120°C for 10 to 12 hours (less effective than a blast drying oven).

• Important Note: Higher temperatures within the drying range yield better results, but do not exceed 160°C to avoid damaging the spool.
• Additional Information: For more details, refer to the Printing tips for Engineering materials on WIKI.

 

Storage Tips:

• Storage Condition: To prevent the filament from absorbing moisture, use an airtight storage container with desiccant during printing.
• For Further Details: Please refer to the Printing tips for Engineering materials on WIKI.

 

Annealing Prints:

• If you need to anneal the prints, please refer to the Technical Data Sheet (TDS) and the WIKI section Work After Printing Finished.

 

Interface Layer:

• To prevent the filament from damaging the printing surface and to promote model adhesion, apply a thin coat of glue stick for best results.

 